INTRODUCTION:
TK172 series is different from traditional TK707 ZrVFe getter. It needs to be heated in vacuum sintering furnace to form sintered body with micro-porous structure, which increases firmness, no loose particles falling off and increased gas adsorption area. The built-in heater can electrically activate the getter, which is convenient and practical. It has significant adsorption effect on O2, N2 and H2. The products are widely used in X-ray tube, infrared detector Dewar bottle, capacitive manometer, argon laser, vacuum circuit breaker, traveling wave tube, which can maintain the vacuum in the tube, absorb harmful gases and prolong the life of the device.
TECHNICAL CHARACTERISTICS:
货号编码 Code | 型号 Type | 外径OD (mm) | 内径ID (mm) | 厚度H (mm) | 总长L (mm) | 粉重 Weight (mg) | ACP724 | TK172/R/8/8 | Φ8.2 | Φ3 | 8 | 15.5 | 800 | ACP723 | TK172/R/14/10 | Φ14.2 | Φ8 | 10 | 25 | 3000 | ACP725 | TK172/R/16/10 | Φ16 | Φ8 | 10 | 17 | 4200 | ACP721 | TK172/R/2/7 | Φ2 | / | 7 | 21 | 80 | ACP722 | TK172/R/3/7 | Φ3 | / | 7 | 21 | 150 | Active condition: 450℃, 10min, < 1 Pa |
WORKING CONDITION:
The shelf life of the getters is 1 year. Unopened products must be stored in a dry, clean environment with a relative temperature of less than 60% and a temperature below 35℃.The product should be used immediately after opening. It is recommended to use it in an environment with a relative humidity of less than 60% and a temperature of less than 30℃; it should not be exposed to the atmosphere for more than 24 hours.